Laser Crystal |
Q-switch Crystal |
Nonliner Crystal |
Nd:YVO4 Crystal Nd:YAG Crystal |
Cr:YAG Crystal |
LBO Crystal BBO Crystal |
Nd:GdV04 Crystal |
|
KTP Crystal |
|
Laser Crystal-YAG Crystal |
|
Features |
- Low Loss at 1.06 mm, High Optical Quality
- Good Mechanical and Thermal Properties
- High Gain, Low Threshold, High Efficiency
|
|
Specifications |
Name |
Nd:YAG |
Doping(atm%) |
0.9%~ 1.1% |
Orientation |
<111> crystalline direction |
Wavefront distortion: |
l/8 per inch @ 633 nm |
Extinction Ratio |
>28dB |
Dimensional Tolerance |
Rods with diameter: +/-0.025 mm , Length:+/-0.5 mm |
Surface quality |
10/5 Scratch / Dig per MIL-O-1380A |
Parallelism |
< 10 arc seconds |
Perpendicularity |
< 5 arc minutes |
Clear Aperture |
>90% |
Flatness |
<l/10 @ 633 nm |
|
|
|
Laser Crystal-Nd:YV04 |
|
Features |
- Low lasing threshold and high slope efficiency
- High absorption over a wide pumping wavelength bandwidth
- Large stimulated emission cross-section at lasing wavelength
- Optically uniaxial and large birefringence emits polarized laser
|
|
Specifications |
Name |
Nd:YVO4 |
Nd: Dopant Level (atm% ) |
0.1 % - 3.0 % |
Wavefront Distortion |
< l/8 at 633 nm |
Scattering Sites |
invisible, probed with a He-Ne laser |
Orientation |
0.5 deg. |
Dimensional Tolerance |
0.1 mm |
End-faces Configuration |
Plano/Plano |
Surface quality |
10/5 Scratch/Dig per MIL-O-13830B |
Flatness |
l/10 at 633 nm |
Clear Aperture |
> Central 90% |
Parallelism |
< 10 arc sec. |
Intrinsic Loss |
< 0.1% cm-1 |
|
|
Laser Crystal-Nd:GdV04 |
|
Features |
- larger absorption and emission cross section
- high thermal conductivity
- high slope efficiency or optical conversion efficiency
- good physical and mechanical properties
|
|
Specifications |
Name |
Nd:GdV04 |
Nd: Doping(atm%): |
0.1%~3 % |
Wavefront Distortion |
< l/8 at 633 nm |
Scattering Sites |
invisible, probed with a He-Ne laser |
Orientation |
+/-0.5degree |
Dimensional Tolerance |
+0.1/-0.1mm |
Surface quality |
10/5 Scratch/Dig per MIL-O-13830B |
Flatness |
l/10 at 633 nm |
Clear Aperture |
> Central 90% |
Parallelism |
< 10 arc sec. |
|
|
Q-switch Crystal-Cr:YAG |
|
Features |
- ideal material for passive Q-switching lasers
- high damage threshold of 500-1000 MW/cm2
- outstandingly suited to replace LiF and Dye which are commonly used for passive Q-switching
- low cost and reduced system size and weight.
|
|
Specifications |
Name |
Cr:YAG |
Formula |
Cr4+:Y3Al5O12 |
Crystal Structure |
Cubic Garnet |
Dopant Level |
0.5 mol% ~ 3 mol% |
Thermal conductivity [W/m/K] |
12.13 |
Hardness |
8.5 (Mohs) |
Damage Threshold |
> 500 MW/cm2 |
Refractive Index |
1.82 @ 1064 nm |
|
|
Nonliner Crystal-LBO |
|
Features |
- broad transparency range from 160nm to 2600nm
- relatively large effective SHG coefficient (about three times that of KDP)
- high damage threshold
- wide acceptance angle and small walk-off
- type I and type II non-critical phase matching (NCPM) in a wide wavelength range
- spectral NCPM near 1300nm
|
|
Specifications |
Name |
LBO |
Crystal structure |
Orthorhombic, Space group Pna21, Point group mm2 |
Lattice parameter |
a=8.4473, b=7.3788,c=5.1395,Z=2 |
Melting point |
About 834 |
Mohs hardness |
6 |
Density |
2.47 g/cm3 |
Thermal conductivity |
3.5W/m/K |
Thermal Expansion coefficient |
ax=10.8x10-5/K, ay= -8.8x10-5/K, az=3.4x10-5/K |
Angle tolerance |
6.54mrad-cm(, Type I,1064 SHG)
7.5C-cm(Type II,1064 SHG) |
|
|
Nonliner Crystal-BBO |
|
Features |
- Broad phase matchable range from 409.6 nm to 3500 nm
- Wide transmission region from 190 nm to 3500 nm
- Large effective second-harmonic-generation (SHG) coefficient
- High damage threshold, wide temperature-bandwidth of about 55C
|
|
Specifications |
Name |
BBO |
Wavefront distortion |
less than l/8 @ 633 nm |
Dimension tolerance |
(W 0.1 mm) x (H 0.1 mm) x (L + 0.2 mm/-0.1 mm) |
Clear aperture |
> 90% central area |
Flatness |
l/8 @ 633 nm |
Scratch/Dig code |
10/5 to MIL-O-13830A |
Parallelism |
better than 20 arc seconds |
Perpendicularity |
5 arc minutes |
Angle tolerance |
D < 0.3, D< 0.3 |
|
|
Nonliner Crystal-KTP |
|
Features |
- Large nonlinear optical coefficient
- Wide angular bandwidth and small walk-off angle
- Broad temperature and spectral bandwidth
- High electro-optic coefficient and low dielectric constant
- Nonhydroscopic, chemically and mechanically stable
|
|
Specifications |
Name |
KTP |
Transmitting wavefront distortion |
less than l/4 @ 633 nm |
Dimension tolerance |
(W 0.1 mm) x (H 0.1 mm) x (L + 0.2 mm/-0.1 mm) |
Clear aperture |
> 90% central area |
Flatness |
1/8 @ 633 nm |
Scratch/Dig code |
10/5 to MIL-O-13830A |
Parallelism |
better than 20 arc seconds |
Perpendicularity |
5 arc minutes |
Angle tolerance |
D < 0.5, D < 0.5 |
Chip |
0.1 mm |
|